Solid Wire Electrode BA-MIG 410 for MIG/MAG Welding
Classification:
EN ISO 14343-A: G 13
SFA 5.9 / AWS A5.9: ER410
Main Application
BA-MIG 410 is a solid wire electrode for GMAW, suitable for welding 13% chromium steels, overlay carbon steels for improved corrosion, erosion and abrasion resistance. Service temperature up to +450 °C.
Pre-heat and inter-pass temperature shall be ≥ 200°C. Main used for surfacing steel mill rolls, furnace and burner parts, turbine parts.
Typical analysis and chemical composition acc. to EN ISO 14343-A and AWS A5.9
| Wire electrode | C | Si | Mn | Mo | Ni | Cr | P | S | Cu total |
|---|---|---|---|---|---|---|---|---|---|
| Typical analysis BA-MIG 410 | 0.10 | 0.4 | 0.4 | 0.2 | 0.1 | 13.0 | 0.015 | 0.015 | 0.2 |
| G 13 acc. to ISO 14343-A | 0.15 | 1.0 | 1.0 | 0.3 | 0.3 | 12.0 - 15.0 | 0.03 | 0.02 | 0.3 |
| ER410 acc. to AWS A5.9 | 0.12 | 0.5 | 0.6 | 0.75 | 0.6 | 11.5 - 13.5 | 0.03 | 0.03 | 0.75 |
All - Weld Metal Mechanical Properties / Welding Data:
|
Heat Treatment |
PWHT: 750°C x 1h |
|
|
Yield Strength Re, N/mm² (ksi) |
≥ 350 (51) |
|
|
Tensile Strength Rm, N/mm² (ksi) |
≥ 450 (65) |
|
|
Elongation A5 [%] |
≥ 17 |
|
|
Impact Energy ISO-V, J (ft lbs) |
+20°C: 47 (34) |
|
|
Current/polarity |
DC + |
|
|
Shielding Gas |
ISO 14175: M12/M13 |
|
Base Materials
1.4000 (X6Cr13); 1.4006 (X12Cr13), AISI 410
Package Forms
Spools BS300/15 kg as standard package form for GMAW wire electrodes.
Diameter
1,0 – 1,6 mm. Sizes and tolerances acc. to ISO 544 and AWS A5.9.
Wire Electrode Surface
Smooth finish free from surface defects and foreign matter.